Journal Information
Vol. 7. Issue 1.
Pages 7-13 (January - March 2018)
Download PDF
More article options
Vol. 7. Issue 1.
Pages 7-13 (January - March 2018)
Original Article
DOI: 10.1016/j.jmrt.2017.02.001
Open Access
Ionic liquid assisted hydrothermal synthesis of TiO2 nanoparticles: photocatalytic and antibacterial activity
Kristappagari Manjunatha, Lakshmi Sagar Reddy Yadavb,c, Thummala Jayalakshmib, Viswanath Reddyd, Hanumanthappa Rajanaikae, Ganganagappa Nagarajub,
Corresponding author

Corresponding author.
a Centre for Nano and Material Sciences, Jain University, Kanakapura, Karnataka 562112, India
b Department of Chemistry, Siddaganga Institute of Technology, Tumkur 572103, India
c Department of Chemistry, BMS Institute of Technology, Bangalore 560064, India
d Department of General Education, Gulf Medical University, Ajman, UAE
e Department of Biotechnology, Tumkur University, Tumkur 572101, India
This item has received

Under a Creative Commons license
Article information
Full Text
Download PDF
Figures (8)
Show moreShow less
Tables (1)
Table 1. Antibacterial activity of TiO2 nanoparticles on pathogenic bacterial strains.

In this work, anatase phase TiO2 nanoparticles have been successfully synthesized at 130°C for 2 days via ionic liquid-assisted hydrothermal method. The obtained products were characterized using various analytical techniques. X-ray diffraction data reveals that sample has anatase TiO2 nanoparticles. FTIR spectrum shows that the presence of ionic liquid and indicates Ti-O-Ti peak at around 456nm and the bands at 1410 and 1581cm−1 indicates C–H in-plane vibrations and stretching of imidazolium ring. UV–Vis spectrum shows maximum band at 272nm due to TiO2 nanoparticles. SEM images show the TiO2 nanoparticles are almost spherical in shape. TEM images reveal that the average diameters of TiO2 nanoparticles are in the range of 35nm. TiO2 nanoparticles exhibited excellent photocatalytic activity for the degradation of methylene blue organic dye. Furthermore, the antibacterial properties of TiO2 nanoparticles were investigated against four bacterial strains using the agar well diffusion method.

Ionic liquid
Antibacterial activity
Full Text

Nanostructured TiO2 as a promising catalyst in the photodegradation of most pollutants in water and air have been extensively studied mainly due to its superior ability of destruction of organic contaminants [1]. It is well known that the properties of nanomaterials majorly depend on their structure and morphology. Now-a-days, synthesis of nanostructures with novel morphologies and functional properties have recently been attracted tremendous attention [2–4]. Generally, nanomaterials are synthesized using molecular solvents such as organic solvents and water. Amongst, only a limited number of molecular solvents can be used and some organic solvents cause environmental pollution [5]. Various methods are available to prepare TiO2 based nanoparticles, such as sol–gel, solvothermal, sonochemical, hydrothermal, chemical vapor deposition, electro-deposition, physical vapor deposition, combustion etc. [6–11]. Here, a different trial has been used which is one of the soft solution method compared to other methods using ionic liquids (ILs) as solvents via hydrothermally.

Over the past two decades, ILs have attracted tremendous attention due to their physical and chemical properties such as low boiling point, large electrochemical window, high thermal stability, negligible vapour pressure, non-volatile and high ionic conductivity [12]. An important aspect of the interaction of ILs with nanoparticle precursors involves the nucleation and growth of nanoparticles. Literature says that, ILs have been successfully used as a reaction media for the synthesis of TiO2 nanomaterials. The most attractive property of ILs for the synthesis of TiO2 nanoparticles is the surfactant-like nature, which inhibits the aggregation of the resultant nanoparticles [13]. Furthermore, the fine-tuning ability of the reactants composition benefits the shape and size controlling over the TiO2 nanoparticles. The above mentioned unique properties of IL make the reactions to conduct in open reactor. The term ‘ionothermal’ has been used to describe reactions that are conducted in ILs at high temperature with ambient pressures. As a result, ionothermal reactions avoid high pressure of hydrothermal or solvothermal reactions and eliminate safety problems related to high pressure [14]. Zhou et al. fabricated macroporous TiO2 architectures via the spontaneous self-assembly of mixture of octadecene and 1-alkyl-3-methyl imidazolium-based ionic liquid as the reaction medium [15]. Nagaraju et al. synthesized ionic liquid-assisted hydrothermal synthesis of TiO2 nanoparticles and its application in photocatalysis [16]. Nakashima et al. reported the synthesis of hollow TiO2 micropores by subjecting a mixture of [BMIM] [PF6], toluene and Ti (OBu)4 to vigorous stirring [17]. Dionysiou et al. [18] prepared mesoporous TiO2 using aqueous solution of titanium tetra isopropoxide and [BMim] [PF6]. Prasad et al. have synthesized TiO2 nanoparticles via sol–gel process and tested for antibacterial activity against gram positive bacteria (Staphylococcus aureus) using Disk diffusion method. They have observed highest activity for Ampicillin and Amikacin which signifies that TiO2 nanoparticles are capable of the antimicrobial action on cephalosporins, beta lactums, macrolids, amino glycosides, lincosamides and glycopeptides [19]. Devi et al. prepared Mn doped TiO2 via sol–gel process and studied the photocatalytic activity of degradation of oxo-fused polycyclic aromatic dye [20]. Thoma et al. have highlighted the comprehensive, multi-disciplinary access for the exploitation of low-cost water remediation methods. Chimie douce and green chemical principles thought to be crucial for making such kind of technologies which are economically viable and socially relevant [21].

Here, we have synthesized TiO2 nanoparticles using ionic liquid assisted hydrothermal method. The obtained product was characterized by various techniques and used for photocatalytic degradation of methylene blue organic dye under solar as well as UV irradiations. We have also examined for antibacterial activities against four bacterial strains using the agar well diffusion method.

2Experimental procedures2.1Synthesis of ionic liquid: 1-butyl-3-methylimidazolium chloride – [BMIM]Cl

The ionic liquid 1-n-butyl-3-methyl imidazolium chloride [BMI.Cl] was prepared using previously described report [12]. 151.5g [1.85mol, 1eq] of freshly distilled N-methyl imidazole, 100mL of acetonitrile and 220g [2.4mol, 1.3eq] of 1-chlorobutane were mixed in three-necked, round-bottomed flask and reflux it to 60°C for 48h. The solution was then cooled to room temperature. The volatile material was removed from the resulting yellow solution under reduced pressure. The remaining light-yellow oil was re-dissolved in dry acetonitrile [250mL] and added dropwise via cannula to a well-stirred solution of 1000mL of dry ethyl acetate and one seed crystal of 1-butyl-3-methylimidazolium chloride, placed in 2000mL round-bottomed flask, equipped with a nitrogen inlet adapter and an overhead mechanical stirrer. The imidazolium salt begins to crystallize exothermically almost immediately, and after the addition of the acetonitrile solution was completed, the flask was cooled at −30°C for 2h.

The supernatant solution was removed via filtration through a filter cannula and the resulting white solid was dried under reduced pressure [0.1mbar, 0.001mm] at 30°C for 6h to afford 1-butyl-3-methylimidazolium chloride. The structure of ionic liquid was as shown in Scheme 1.

Scheme 1.

Structure of 1-butyl-3-methyl imidazolium chloride – [BMIM] Cl.

2.2Synthesis of TiO2 nanoparticles:

In a typical synthesis, 0.4g TiO2 P25 was added to 5mL H2O2 taken in Teflon tube. The mixed solution was then gently stirred and then 35mL H2O was added slowly in to the Teflon tube followed by 2mL HNO3 and 0.5g butyl-methyl imidazolium chloride BMI. Cl with constant stirring. Then the whole mixture was subjected to hydrothermal treatment at 130°C for 2 days. After the reaction was complete, the autoclave was cooled to room temperature naturally. The product obtained from centrifugation was washed several times with water followed by ethanol. The obtained product was mixed with acetonitrile and stirred overnight to remove ILs. The final product obtained from centrifugation was dried in an oven at 80°C overnight.

2.3Procedure for photocatalytic degradation of dye

Photocatalytic experiments were carried out in a 150mm×75mm batch reactor. An aqueous suspension was prepared by dispersing 100mg of TiO2 nanoparticles in 100mL of 10ppm methylene blue dye solution. During the photocatalytic experiments the slurry composed of dye solution and catalyst were placed in the reactor and stirred magnetically for agitation with simultaneous exposure to sunlight and UV light. The known volume (10mL) of the exposed solution was withdrawn at specific interval of time (30min). TiO2 nanoparticles were removed from the solution by centrifugation to assess the extent of degradation. The dye concentration was measured using a spectrophotometer at 664nm. The % of degradation can be determined using the following formula.

where X is the % of degradation where Ci and Cf are the initial and final dye concentrations respectively. The experiment was carried out by varying various parameters like sunlight/UV light irradiation time.

2.4Procedure for antibacterial activity

Antibacterial activity was screened by agar well diffusion method [22] against four bacterial strains namely Gram-ve Klebsiella aerogenes NCIM-2098, Escherichia coli NCIM-5051, Pseudomonas desmolyticum NCIM-2028 and Gram+ve bacteria Staphylococcus aureus NCIM-5022. Nutrient agar plates were prepared and swabbed using sterile L-shaped glass rod with 100μL of 24h mature broth culture of individual bacterial strains. The wells were made by using sterile cork borer (6mm). Wells were created into each petri-plates. Different concentrations of TiO2 nanoparticles (1000 and 1500μg/well) were used to assess the activity of the nanoparticles. The TiO2 nanoparticles were dispersed in sterile water and it was used as negative control and simultaneously the standard antibiotics Ciprofloxacin (5μg/50μL) (Hi Media, Mumbai, India) as positive control were tested against the bacterial pathogens. Then the plates were incubated at 37°C for 24–36h. The zone inhibition of every well measured was in millimeter. Triplicates were maintained in every concentration and the average values were calculated for the ultimate antibacterial activity. The bacterial rate (K) could be calculated by the following equation.

where A and B are the number of bacterial colonies corresponding to the positive control group and the sample group, respectively.


The crystal structure and composition of TiO2 nanoparticles were determined by Powder X-ray diffraction (PXRD), data were recorded on Philips X’pert PRO PANalytical X ray diffractometer with graphite monochromatized Cu-Kα (1.5418Å) radiation. The Fourier transform infrared (FTIR) spectrum of the sample is collected using Bruker Alpha-P spectrometer. The absorption spectrum of the sample is measured on a UV-1800 UV-Vis spectrometer (UV-Vis). The surface morphology was examined by Carl Zeiss ultra 55 scanning electron microscopy (SEM) and transmission electron microscopy (TEM) was performed using JEOL JEM 1200 Ex operating at 100kV.

3Results and discussion

Fig. 1 shows the XRD pattern of TiO2 nanoparticles prepared at 130°C for 2 days. All the diffraction peaks of the product can be indexed to anatase form of TiO2 nanoparticles (JCPDS no. 021–1272), a=b=3.785Å, c=9.513Å, 141/amd). The average diameter of NPs was found to be 40nm and was calculated from Debye-Scherrer's equation:

where D is the crystal size and λ is the wavelength of X-ray radiation (1.5418Å), β is the full width half maximum of diffraction peak and θ is the scattering angle.

Fig. 1.

XRD pattern of TiO2 nanoparticles.


The FTIR spectrum of the as-prepared sample is shown in Fig. 2. The bands at 1581 and 1410cm−1 can be assigned to C–H stretching and in-plane vibrations of the imidazolium ring [23]. The bands at 616 and 644cm−1 can be attributed to aliphatic (organic compounds) in-plane vibrations. The bands at 924 and 1010cm−1 are due to the respective out of plane vibrations of the organic cations, respectively. The band at 456cm−1 is due to the presence of Ti–O–Ti.

Fig. 2.

FT-IR spectra of TiO2 nanoparticles.


The UV–Vis spectrum of the TiO2 nanoparticles in Fig. 3, which shows a maximum absorbance band at 272nm. The band at around 272nm can be assigned to the TiO2 nanoparticles (Eg=3.7eV) which shows the shift of the band toward lower wavelength which is called blue shift when compared to that of bulk TiO2 (Eg=3.2eV). Observation of blue shift is due to reduction of size (quantum size) and confinement effects [16,24].

Fig. 3.

UV-visible spectrum of TiO2 nanoparticles.


The SEM images of the as-prepared sample are shown in Fig. 4. It Shows the TiO2 nanoparticles are almost spherical in shape. The morphology is further confirmed by TEM and is shown in Fig. 5. It shows of TiO2 nanoparticles are almost oval in shape and the average size of the TiO2 nanoparticles are found to be 35nm.

Fig. 4.

SEM images of TiO2 nanoparticles.

Fig. 5.

TEM images of TiO2 nanoparticles.

4Effect of different nature of light source on photocatalytic activity

Fig. 6 shows the effect of different light source on photocatalytic degradation of methylene blue dye. Two different light sources are used namely sunlight and UV-light. The experiment was carried out by dispersing 100mg of TiO2 nanoparticles in 100mL of 10ppm methylene blue dye solution. From Fig. 6, it is clearly shown that photocatalytic degradation of the dye was more in UV-light than in sunlight. This is due to the fact that the absorbance band of TiO2 nanoparticles appeared in UV region.

Fig. 6.

Photocatalytic photo degradation of Methylene blue using TiO2 nanoparticles.


The photocatalytic degradation of methylene blue organic dye has been studied by several researchers [25,26] and the mechanistic scheme leading to the photocatalytic degradation of the methylene blue organic dye is shown below.

TiO2+hv (UV)TiO2 (eCB+hVB+)
TiO2 (hVB+)+H2OTiO2+H++OH
TiO2 (hVB+)+OHTiO2+OH
TiO2 (eCB)+O2TiO2+O2
Dye+OH → degradation products
Dye+hVB+oxidation products
Dye+eCBreduction products
where hv is the photon energy required to Ti excite the semiconductor electron from the valence band (VB) region to conduction band (CB) region. From the above characterization results high crystallinity, small size provides sufficient number of active sites to adsorb dye molecules on the surface of the sample for degradation which enhances the degradation. Absorbance spectra play a crucial role in selecting the suitable catalyst for photocatalysis based on absorbance band.

5Antibacterial activity studies

The antibacterial properties of the TiO2 nanoparticles is evaluated against Gram-ve K. aerogenes, E. coli, P. desmolyticum. Gram+ve bacteria S. aureus using agar well diffusion method. In this method, the TiO2 nanoparticles showed significant antibacterial activity on all the four bacterial strains. The bacterial strains of Gram-ve K. aerogenes, E. coli, P. desmolyticum. Gram+ve bacteria S. aureus with 500 and 1000μg concentration of TiO2 nanoparticles show the zone of inhibition as shown in Fig. 7. The data is shown in Table 1. The mechanism is as follows “The antibacterial activity of TiO2 NPs shows the maximum inhibition zone was observed in the presence of nano-TiO2. Nanomaterials are known to inactivate cellular enzymes and DNA by binding to electron-donating groups such as Carboxylates, Amides, Indoles, Hydroxyls, Thiols, etc. They cause little pores in bacterial cell walls, leading to increased permeability and cell death. Based on this study, nano-TiO2 has an efficient antibacterial effect and can be used as an antibacterial agent’.

Fig. 7.

Zone of inhibition of (a) Klebsiella aerogenes, (b) Escherichia coli, (c) Staphylococcus aureus and (d) Pseudomonas desmolyticum.

Table 1.

Antibacterial activity of TiO2 nanoparticles on pathogenic bacterial strains.

Sl. no  Treatment  Klebsiella aerogenes (B1) (Mean±SE)  Escherichia coli (B2) (Mean±SE)  Staphyloccus aureus (B4) (Mean±SE)  Pseudomonas desmolyticum (B5) (Mean±SE) 
Standard (5μg/50μL)  8.33±0.33b  9.00±0.00  9.67±0.33b  12.67±0.33b 
II  TiO2 (500μg/50μL)  2.67±0.33b  1.67±0.33b  2.33±0.33b  1.00±0.00 
III  TiO2 (1000μg/100μL)  3.67±0.33b  2.67±0.33b  4.00±0.00  2.33±0.33b 

Values are the mean±SE of inhibition zone in mm. (a) and (b) represent statistical significance.

aP<0.05 as compared with the control group.


P<0.01 as compared with the control group.


We have successfully synthesized TiO2 nanoparticles using functionalized ionic liquid via hydrothermal method. PXRD confirmed the existence of anatase phase TiO2 nanoparticles. The average size of the TiO2 nanoparticles from TEM were found to be 35nm. TiO2 nanoparticles exhibited excellent photocatalysis for the degradation of methylene blue organic dye. The antibacterial properties of TiO2 nanoparticles were investigated by their bactericidal activities against four bacterial strains using the agar well diffusion method.

Conflicts of interest

The authors declare no conflicts of interest.


One of the author Nagaraju thanks BRNS-BARC, DAE, Bombay, Govt. of India for financial support to carry out the research work (37(2)/14/25/2015/BRNS dated 03/12/2015). Dr. K. Manjunath and Dr. G. Nagaraju thank CNPq-TWAS and UFRGS for providing the fellowships and facilities. L. S. Reddy Yadav acknowledges BMSIT for providing financial support and encouragement for the research work.

I.A. Omo, P. Fitzpatrick.
Heterogeneous photocatalysis: recent advances and applications.
Catalysts, 3 (2013), pp. 189-218
H.S. Yun, K. Miyazawa, H. Zhou, M. Kuwabara.
synthesis of mesoporous thin TiO2 films with hexagonal pore structures using triblock copolymer templates.
Adv Mater, 13 (2001), pp. 1377-1380
S. Haseloh, S.Y. Choi, M. Mamak, N. Coombs, S. Petrov, N. Chopra, et al.
Synthesis of mesoporous titania networks consisting of anatase nanowires by templating of bacterial cellulose membranes.
Chem. Commun., 7 (2004), pp. 1460-1470
M. Adachi, Y. Murata, J. Takao.
Highly efficient dye-sensitized solar cells with a titania thin-film electrode composed of a network structure of single-crystal-like TiO2 nanowires made by the “oriented attachment” mechanism.
J Am Chem Soc, 126 (2004), pp. 14943-14949
X. Liu, J. Maand, W. Zheng.
Catalysis in ionic liquirds: from catalyst synthesis to application.
Rev. Adv. Mater. Sci., 27 (2011), pp. 43-50
H. Lin, P.W. Oliveira, I. Grobelsek, A. Haettich.
The synthesis of anatase TiO2 nanoparticles by solvothermal method using ionic liquid as addtive.
Z Anorg Allg Chem, 636 (2010), pp. 1947-1954
K. Manjunath, V.S. Souza, T. Ramakrishnappa, G. Nagaraju, J.D. Scholten, J. Dupont.
Heterojunction CuO-TiO2 nanocomposite synthesis for significant photocatalytic hydrogen production.
Mater Res Express, 3 (2016), pp. 115904
K. Manjunath, V.S. Souza, Nagaraju g, L.S.J. Marcos, J. Dupont, T. Ramakrishnappa.
Superior activity of the CuS-TiO2/Pt hybrid nanostructure towards visible light induced hydrogen production.
New J Chem, 40 (2016), pp. 10172-10180
G. Nagaraju, T.N. Ravishankar, K. Manjunatha, S. Sarkar, H. Nagabhushana, R. Goncalves, et al.
Ionothermal synthesis of TiO2 nanoparticles: photocatalytic hydrogen generation.
Mater Lett, 109 (2013), pp. 27-30
G. Nagaraju, K. Manjunath, S. Sarkar, E. Gunter, S.R. Teixeira, J. Dupont.
TiO2-RGO hybrid nanomaterials for enhanced water splitting reaction.
Int J Hydrogen Energy, 40 (2015), pp. 12209-12216
K. Manjunath, V.S. Souza, g Nagaraju, J.D. Scholten, S.R. Teixeira, J. Dupont, et al.
Mesoporous foam TiO2 nanomaterials for effective hydrogen production.
Chem A Eur J, 21 (2015), pp. 17624-17630
J. Dupont, R.F. De Souza, P.A.Z. Suarez.
Ionic liquid (molten salt) phase organometallic catalysis.
Chem Rev, 102 (2002), pp. 3667-3692
D.B. Antonietti, Y.Z. Kuang, Y. Zhou.
Ionic liquids for the convenient synthesis of functional nanoparticles and other inorganic nanostructures.
Angew Chem Int Ed Engl, 43 (2004), pp. 4988-4992
A. Taubert, Z.Z. Li.
Inorganic materials from ionic liquids.
Dalton Trans, (2007), pp. 723-727
Z. Zhou, G.A. Ma, Q. Baker.
One-pot synthesis of uniform TiO2 nanorods and monodisperse TiO2 microspheres and their light scattering properties.
Langmuir, 25 (2009), pp. 801-806
G. Nagaraju, K. Manjunath, H. Nagabhushana, G. Ebeling, J. Dupont.
Ionic liquid-assisted hydrothermal synthesis of TiO2 nanoparticles and its application in photocatalysis J.
Mater Sci, 48 (2013), pp. 8420-8426
T. Nakashima, N. Kimizuka.
Interfacial synthesis of hollow TiO2 microspheres in ionic liquids.
J Am Chem Soc, 125 (2003), pp. 6386-6387
K.S. Yoo, H. Choi.
Synthesis of anatase nanostructured TiO2 particles at low temperature using ionic liquid for photocatalysis.
Catal Commun, 6 (2005), pp. 259-262
D. Prasad, N. Kottam, H. Nagabhushana, C.R. Girija, B.M. Nagabhushana.
Nanostructured TiO2 prepared through sol–gel method enhances the activity of antibiotics against Gram positive bacteria.
J NanoSci NanoEng Appl, 2 (2012), pp. 1-5
L.G. Devi, N. Kottam, S.G. Kumar.
Preparation and characterization of Mn doped titanates with bicrystalline framework: correlation of crystallite size with synergistic effect on photo catalytic activity.
J Phy Chem C, 113 (2009), pp. 15593-15601
T. Thoma, N. Kottam.
Combining “chimie douce” and green principles for the developing world: improving industrial viability of photocatalytic water remediation.
Chem. Eng. Sci., 102 (2013), pp. 283-288
C. Perez, M. Paul.
An antibiotic assay by the agar well-diffusion method.
Acta Biol Med Exp, 15 (1990), pp. 113-115
X. Chen, S.S. Mao.
Titanium dioxide nanomaterials: synthesis, properties, modifications, and applications.
Chem Rev, 107 (2007), pp. 2891-2959
G. Paul, A. Choudhury, C.N.R. Rao.
A novel polyoxometalate chain formed from heteropolyanion building blocks and rare earth metal ion linkers: [La(H2O)7Al(OH)6Mo6O18]n·4nH2O.
J Chem Soc Dalton Trans, 20 (2002), pp. 3781-3837
S. Lakshmi, R. Ranganathan, S. Fujita.
Study on TiO2-mediated photocatalytic degradation of methylene blue.
J Photochem Photobiol A: Chem, 88 (1995), pp. 163-167
A. Houas, H. Lachheb, M. Ksibi.
Photocatalytic degradation pathway of methylene blue in water.
Appl Catal B: Environ, 31 (2001), pp. 145-157
Copyright © 2018. Brazilian Metallurgical, Materials and Mining Association
Journal of Materials Research and Technology

Subscribe to our newsletter

Article options
Cookies policy
To improve our services and products, we use cookies (own or third parties authorized) to show advertising related to client preferences through the analyses of navigation customer behavior. Continuing navigation will be considered as acceptance of this use. You can change the settings or obtain more information by clicking here.